Lustran® ABS PG 298

丙烯腈丁二烯苯乙烯

 

INEOS ABS (USA)

 

Technical Data

 

产品说明

 

Lustran ABS PG 298 resin is a plateable grade of ABS (acrylonitrile butadiene styrene) for use in automotive and general-purpose applications. This injection molding grade was designed specifically for improved thermocycle performance and outstanding plate adhesion. It provides a unique combination of flow and rigidity, with increased scratch resistance and increased resistance to deformation on plating racks. The resin is available in gray color only.

 

Lustran ABS PG 298 resin is used in the automotive industry for plated grilles, wheel covers, exterior mirror housings, and exterior trim. It is also used for decorative parts in the appliance and lawn and garden markets. As with any product, use of Lustran ABS PG 298 resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet (English)

UL 黄卡 2 •  E44741-633567

搜索 UL 黄卡 •  INEOS ABS (USA)

•  Lustran® ABS

供货地区 • 北美洲

特性 • 尺寸稳定性良好 • 良好的流动性 • 耐刮擦性

• 可电镀 • 良好粘结性 • 中等硬度

用途 • 汽车领域的应用 • 汽车外部零件

机构评级 • EC 1907/2006 (REACH)

外观 • 灰色

形式 • 粒子

加工方法 • 注射成型

 

物理性能 额定值单位制 测试方法

比重 1.06g/cm³ ASTM D792

特定体积 0.940cm³/g ASTM D792

熔流率（熔体流动速率） ASTM D1238

220°C/10.0 kg 19g/10 min

230°C/3.8 kg 5.0g/10 min

收缩率 - 流动 0.40 到 0.60% ASTM D955

机械性能 额定值单位制 测试方法

拉伸模量 ASTM D638

-- 4 7580MPa

-- 5 2770MPa

抗张强度

屈服 40.0MPa ASTM D638

屈服 43.0MPa ISO 527-2

弯曲模量

-- 4 12500MPa ASTM D790

-- 5 2830MPa ASTM D790

-- 2730MPa ISO 178

弯曲强度 ASTM D790

屈服 4 117MPa

屈服 5 78.6MPa

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度

23°C, 3.18 mm 170J/m ASTM D256

-40°C 6 6.4kJ/m² ISO 180/1A

23°C 6 14kJ/m² ISO 180/1A

 

 

 

Lustran® ABS PG 298

丙烯腈丁二烯苯乙烯

INEOS ABS (USA)

硬度 额定值单位制 测试方法

洛氏硬度 (R 级) 110 ASTM D785

热性能 额定值单位制 测试方法

载荷下热变形温度 ASTM D648

0.45 MPa, 未退火, 3.18 mm 91.1°C

0.45 MPa, 未退火, 12.7 mm, 模压成型 103°C

0.45 MPa, 退火, 12.7 mm 100°C

1.8 MPa, 未退火, 3.18 mm 83.9°C

1.8 MPa, 未退火, 12.7 mm, 模压成型 98.3°C

1.8 MPa, 退火, 12.7 mm 97.2°C

维卡软化温度

-- 110°C ASTM D1525 7

-- 36.6°C ISO 306/B50

可燃性 额定值单位制 测试方法

燃烧速率 8 (2.01 mm) 48mm/min SAE J1685

注射 额定值单位制

干燥温度

A 82.2 到 87.8°C

B 71.1 到 76.7°C

干燥时间

A 2.0hr

B 4.0hr

建议的最大水分含量 < 0.10%

建议注射量 50 到 75%

建议的最大回制料比例 20%

料筒后部温度 243 到 252°C

料筒中部温度 249 到 257°C

料筒前部温度 254 到 263°C

射嘴温度 254 到 263°C

加工（熔体）温度 260 到 277°C

模具温度 48.9 到 60.0°C

注塑压力 68.9 到 110MPa

注射速度 慢

背压 0.345 到 0.689MPa

锁模力 2.8 到 5.5kN/cm²

螺杆长径比 20.0:1.0

螺杆压缩比 2.5:1.0

注射说明

Hold Pressure: 50 to 75% of Injection Pressure

Screw Speed: Moderate

备注

 

 